Determination of manganese in high purity manganese powder
Metal manganese is easily oxidized in the air and forms the oxide film on its surface. It will affect its physical properties, chemical properties and performance. When it is used in powder state, metal powder has a large surface area, and its oxidation is intensified. According to technical conditions, some provisions declare that the manganese content should not be less than 99.00% in manganese powder. Therefore it is necessary to have cooled determination of manganese content in manganese powder.
Separation method for the reduction of manganese and manganese metal in other metallurgical intermediate products although many reports, but does not apply to high-purity manganese powder. Relatively large radius of the ion of this method as an oxidant, it is difficult to spread to the surface of the metal through the metal surface into the membrane, and the reaction products are solid phase. It further hinders dissolution. The metal manganese can not be completely leaching. On the other hand, the original solvent such as Br methanol, the compounds of manganese on the surface of the fine into a very strong ability to dissolve. It lost its selection and there is no practical value.
Manganese powder
in the surface oxide film oxides MnO and Mn3O4, there is almost no other high
manganese oxide. Dissolved manganese metal solvent, must be maintained at pH
8-8.7, the leaching system should not be there is a strong oxidizing or
reducing agent. In this condition, MnO, with the metal manganese is dissolved,
Mn3O4 and other high manganese oxide solution in the ammonium salt solution (It
is fastest in NH4NO3 solution), and brown manganese oxide is not dissolved. Due
to the buffering effect of the ammonium salt, can keep the solution at pH
8-8.7. After leaching 100mL
Placing
In : metal powder